8m borosilicate honeyqomb spin casting: Material developments

B. H. Olbert, J. R.P. Angel, L. U. Goble

Research output: Contribution to journalConference articlepeer-review

Abstract

Creep and strength of candidate glass contact refractories for honeycomb casting molds were measured at 1200 C. Based on performance and cost, one material, Rex Roto Corp.'s R1162-17 speciality fiber mix, was chosen for the Steward's first 3.5m casting mold. More extensive measurements of firing shrinkage, thermal expansion, room temperature Young's Modulus, bulk density, and creep were carried out on R1162-17 samples cut from hexagonal box preforms. Test results indicate that R1162-17 hex boxes have acceptable creep resistance and the potential strength to withstand hydrostatic loading up to 66cm of borosilicate melt. In November of 1987, blocks of a low-expansion borosilicate glass, Corning Code 7761, was spin cast into a 1.2m honeycomb for the Smithsonian Astrophysical Observatory. The casting contained a relatively high density of small-scale striae and small bubbles along the remelted block surfaces. Origin of the small bubbles was traced to graphite particles imbedded in the glass surface during the forming operation. In spite of small-scale striae, the measured expansion coefficient variation over spacial scales greater than 1mm was less than t7x10~9/c.

Original languageEnglish (US)
Pages (from-to)268-276
Number of pages9
JournalProceedings of SPIE - The International Society for Optical Engineering
Volume966
StatePublished - Jan 29 1989
EventAdvances in Fabrication and Metrology for Optics and Large Optics 1988 - San Diego, United States
Duration: Aug 15 1988Aug 18 1988

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Computer Science Applications
  • Applied Mathematics
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of '8m borosilicate honeyqomb spin casting: Material developments'. Together they form a unique fingerprint.

Cite this