Aggressive diamond characterization and wear analysis during chemical mechanical planarization

Changhong Wu, Yun Zhuang, Xiaoyan Liao, Yubo Jiao, Yasa Adi Sampurno, Siannie Theng, Fred Sun, Ananth Naman, Ara Philipossian

Research output: Contribution to journalArticle

8 Scopus citations

Abstract

A 3M A3700 diamond disk was used to condition a Cabot Microelectronics Corporation D100 pad for 30 hours, and wear on its aggressive diamonds was analyzed. The top 20 aggressive diamonds for two perpendicular disk orientations were identified before wafer polishing, as well as after 15-hour and 30-hour polishing. Results showed that the original top 20 aggressive diamonds identified before polishing were subjected to wear after the first 15-hour polishing as the furrow surface area that they generated decreased dramatically by 47%. As these original aggressive diamonds were worn, seven new aggressive diamonds were "born" and joined the new top 20 list for both disk orientations. After the second 15-hour wafer polishing, the furrow surface area of these new top 20 aggressive diamonds did not change significantly. The furrow surface area created by all the active diamonds exhibited the same trend as the top 20 aggressive diamonds, confirming that most pad conditioning work was performed by these aggressive diamonds and that the disk lost its aggressiveness in the first 15 hours of polishing and then maintained its aggressiveness during the second 15 hours.

Original languageEnglish (US)
Pages (from-to)P36-P41
JournalECS Journal of Solid State Science and Technology
Volume2
Issue number1
DOIs
StatePublished - Nov 18 2013

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials

Fingerprint Dive into the research topics of 'Aggressive diamond characterization and wear analysis during chemical mechanical planarization'. Together they form a unique fingerprint.

  • Cite this