Degradation of Ir-Ta oxide coated Ti anodes in sulfuric acid solutions containing fluoride

Dongni Ma, Vanda Ngo, Srini Raghavan, Scot Sandoval

Research output: Contribution to journalArticle

Abstract

The lifetime of IrO2-Ta2O5 coated titanium anodes has been investigated using a galvanostatic accelerated life test (ALT) method in 2 M (2000 mol/m3) H2SO4 solutions containing fluoride. Fluoride addition in the concentration range of 25−200 ppm significantly reduces the lifetime of films through localized thinning and in some cases, complete removal of film. While the presence of fluoride does not affect the overpotential for oxygen evolution, it lowers the efficacy of oxygen evolution. Complexation of fluoride by aluminum ions reduces the deleterious effects of fluoride. Based on thermodynamic and XPS analyses, a degradation mechanism has been proposed.

Original languageEnglish (US)
Article number108358
JournalCorrosion Science
DOIs
StateAccepted/In press - Jan 1 2019

Keywords

  • Acid corrosion (C)
  • Galvanostatic (B)
  • Oxide coatings (C)
  • Pourbaix diagram (C)
  • Tantalum-iridium oxide (A)
  • XPS (B)

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)
  • Materials Science(all)

Fingerprint Dive into the research topics of 'Degradation of Ir-Ta oxide coated Ti anodes in sulfuric acid solutions containing fluoride'. Together they form a unique fingerprint.

  • Cite this