Frequency upconversion of Er3+ in Ga2S 3-GeS2-La2S3 glasses

Kohei Kadono, Masahide Takahashi, Hiroto Higuchi, Masanori Shojiya, Tomoko Ohtsuki, Yoji Kawamoto, Nasser Peyghambarian

Research output: Contribution to journalConference article

2 Scopus citations

Abstract

Glasses containing Er3+ ions of 0.3 to 7 cation mol percent were prepared in the system of Ga2S3-GeS2-LaS 3. Frequency upconversion spectra of Er3+ in the glasses were measured under the excitation at 800 nm and 980 nm. Green emissions at 533 nm (2H11/2yields4I15/2) and 552 nm (4S3/2yields4I15/2), and red emission at 665 nm (4F9/2yields4I 15/2) were observed.In addition to these emission bands, 497 nm emission assigned to the 4F7/2yields4I 15/2 transition was observed. The spectral properties are analyzed from the view points of low phonon energy property and high refractive index.

Original languageEnglish (US)
Pages (from-to)25-31
Number of pages7
JournalProceedings of SPIE - The International Society for Optical Engineering
Volume2996
DOIs
StatePublished - Dec 1 1997
EventRare-Earth-Doped Devices - San Jose, CA, United States
Duration: Feb 10 1997Feb 10 1997

Keywords

  • Erbium
  • Multiphonon relaxation
  • Nonoxide glass
  • Phonon energy
  • Sulfide glass
  • Upconversion

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Computer Science Applications
  • Applied Mathematics
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Frequency upconversion of Er<sup>3+</sup> in Ga<sub>2</sub>S <sub>3</sub>-GeS<sub>2</sub>-La<sub>2</sub>S<sub>3</sub> glasses'. Together they form a unique fingerprint.

  • Cite this