Heterogeneity, spatial correlations, size effects and dissipated energy in brittle materials

Research output: Contribution to journalArticle

9 Citations (Scopus)

Abstract

The present study was inspired by recent experiments performed by the second author and co-workers where heterogeneity in a brittle material was investigated by ultrasonic scanning. The experiments showed an irregular pattern of material heterogeneity even before any external load was applied on the specimens. Under increasing uniaxial compressive load, the initial heterogeneity pattern evolved, and finally a macro crack network formed. In a previous study the finite element method was used in conjunction with a theory for distributed damage to study the effects of material heterogeneity numerically. Both experiments and finite element analysis showed that initially "strong" regions dissipated energy at a much higher rate than "weak" ones. However, the FEM is more suitable and efficient when material response can be homogenized and deformation gradients are not prominent. If this is not the case, or if one is interested in understanding and/or modeling the effects of heterogeneity and crack network formation, a lattice approach may be more suitable. In this study, the predictions of the lattice-based numerical approach are compared to experimental data on crack formation. Recently, a branch of statistical physics has focused on statistical modeling of materials. Here, it is attempted to "connect" this approach to continuum solid mechanics theories. Important connections are believed to be spatial correlations and localization phenomena in materials, as discussed herein. Using random fields to represent initial heterogeneity, the effects of spatial correlations on size effects, dissipated energy and on crack formation are studied. Results from two random field generation algorithms are reported, and, surprisingly, dissipated energy and crack network characteristics were dependent on the algorithm. Both provide a good description of the well-known size effect observed in brittle materials. However, notable differences between the two algorithms with respect to localization of deformation were identified.

Original languageEnglish (US)
Pages (from-to)103-118
Number of pages16
JournalMechanics of Materials
Volume18
Issue number2
DOIs
StatePublished - 1994

Fingerprint

brittle materials
Brittleness
Cracks
Finite element method
Crack initiation
cracks
crack initiation
energy
solid mechanics
Experiments
continuum mechanics
Macros
Mechanics
Physics
Ultrasonics
finite element method
Scanning
ultrasonics
damage
gradients

ASJC Scopus subject areas

  • Mechanics of Materials

Cite this

@article{c71afce3a38e4eb6b4748b0181fe5bea,
title = "Heterogeneity, spatial correlations, size effects and dissipated energy in brittle materials",
abstract = "The present study was inspired by recent experiments performed by the second author and co-workers where heterogeneity in a brittle material was investigated by ultrasonic scanning. The experiments showed an irregular pattern of material heterogeneity even before any external load was applied on the specimens. Under increasing uniaxial compressive load, the initial heterogeneity pattern evolved, and finally a macro crack network formed. In a previous study the finite element method was used in conjunction with a theory for distributed damage to study the effects of material heterogeneity numerically. Both experiments and finite element analysis showed that initially {"}strong{"} regions dissipated energy at a much higher rate than {"}weak{"} ones. However, the FEM is more suitable and efficient when material response can be homogenized and deformation gradients are not prominent. If this is not the case, or if one is interested in understanding and/or modeling the effects of heterogeneity and crack network formation, a lattice approach may be more suitable. In this study, the predictions of the lattice-based numerical approach are compared to experimental data on crack formation. Recently, a branch of statistical physics has focused on statistical modeling of materials. Here, it is attempted to {"}connect{"} this approach to continuum solid mechanics theories. Important connections are believed to be spatial correlations and localization phenomena in materials, as discussed herein. Using random fields to represent initial heterogeneity, the effects of spatial correlations on size effects, dissipated energy and on crack formation are studied. Results from two random field generation algorithms are reported, and, surprisingly, dissipated energy and crack network characteristics were dependent on the algorithm. Both provide a good description of the well-known size effect observed in brittle materials. However, notable differences between the two algorithms with respect to localization of deformation were identified.",
author = "Huanping Dai and Frantziskonis, {George N}",
year = "1994",
doi = "10.1016/0167-6636(94)00004-2",
language = "English (US)",
volume = "18",
pages = "103--118",
journal = "Mechanics of Materials",
issn = "0167-6636",
publisher = "Elsevier",
number = "2",

}

TY - JOUR

T1 - Heterogeneity, spatial correlations, size effects and dissipated energy in brittle materials

AU - Dai, Huanping

AU - Frantziskonis, George N

PY - 1994

Y1 - 1994

N2 - The present study was inspired by recent experiments performed by the second author and co-workers where heterogeneity in a brittle material was investigated by ultrasonic scanning. The experiments showed an irregular pattern of material heterogeneity even before any external load was applied on the specimens. Under increasing uniaxial compressive load, the initial heterogeneity pattern evolved, and finally a macro crack network formed. In a previous study the finite element method was used in conjunction with a theory for distributed damage to study the effects of material heterogeneity numerically. Both experiments and finite element analysis showed that initially "strong" regions dissipated energy at a much higher rate than "weak" ones. However, the FEM is more suitable and efficient when material response can be homogenized and deformation gradients are not prominent. If this is not the case, or if one is interested in understanding and/or modeling the effects of heterogeneity and crack network formation, a lattice approach may be more suitable. In this study, the predictions of the lattice-based numerical approach are compared to experimental data on crack formation. Recently, a branch of statistical physics has focused on statistical modeling of materials. Here, it is attempted to "connect" this approach to continuum solid mechanics theories. Important connections are believed to be spatial correlations and localization phenomena in materials, as discussed herein. Using random fields to represent initial heterogeneity, the effects of spatial correlations on size effects, dissipated energy and on crack formation are studied. Results from two random field generation algorithms are reported, and, surprisingly, dissipated energy and crack network characteristics were dependent on the algorithm. Both provide a good description of the well-known size effect observed in brittle materials. However, notable differences between the two algorithms with respect to localization of deformation were identified.

AB - The present study was inspired by recent experiments performed by the second author and co-workers where heterogeneity in a brittle material was investigated by ultrasonic scanning. The experiments showed an irregular pattern of material heterogeneity even before any external load was applied on the specimens. Under increasing uniaxial compressive load, the initial heterogeneity pattern evolved, and finally a macro crack network formed. In a previous study the finite element method was used in conjunction with a theory for distributed damage to study the effects of material heterogeneity numerically. Both experiments and finite element analysis showed that initially "strong" regions dissipated energy at a much higher rate than "weak" ones. However, the FEM is more suitable and efficient when material response can be homogenized and deformation gradients are not prominent. If this is not the case, or if one is interested in understanding and/or modeling the effects of heterogeneity and crack network formation, a lattice approach may be more suitable. In this study, the predictions of the lattice-based numerical approach are compared to experimental data on crack formation. Recently, a branch of statistical physics has focused on statistical modeling of materials. Here, it is attempted to "connect" this approach to continuum solid mechanics theories. Important connections are believed to be spatial correlations and localization phenomena in materials, as discussed herein. Using random fields to represent initial heterogeneity, the effects of spatial correlations on size effects, dissipated energy and on crack formation are studied. Results from two random field generation algorithms are reported, and, surprisingly, dissipated energy and crack network characteristics were dependent on the algorithm. Both provide a good description of the well-known size effect observed in brittle materials. However, notable differences between the two algorithms with respect to localization of deformation were identified.

UR - http://www.scopus.com/inward/record.url?scp=0028465707&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0028465707&partnerID=8YFLogxK

U2 - 10.1016/0167-6636(94)00004-2

DO - 10.1016/0167-6636(94)00004-2

M3 - Article

AN - SCOPUS:0028465707

VL - 18

SP - 103

EP - 118

JO - Mechanics of Materials

JF - Mechanics of Materials

SN - 0167-6636

IS - 2

ER -